Stainless steels
FERVEO INX 316L R 17
covered electrode · stick electrodeCatalogue only
AWS class
E316L-17
EN ISO class
E 19 12 3 L R 32
Tensile strength (Rm)
540–670 MPa
Classification
| AWS class | E316L-17 |
|---|---|
| EN ISO class | E 19 12 3 L R 32 |
Purpose
- Same Cr-Ni-Mo 19/11.5/2.6 class as INX 316L R 16, -17 coating variant — same use in tanks and piping for food, textile, chemical and paint industry.
Why it works
Same core and chemistry as INX 316L R 16; the -17 rutile coating variant is the catalog version for this diameter/packaging, with the same stated welding behavior and acid resistance.
Fields of application
- AISI 316, 316L, 316Cb, 316Ti and equivalent Cr-Ni-Mo steels.
- Tanks, piping and equipment in food, textile, chemical and paint industry.
Chemical composition
| Element | Typical, % |
|---|---|
| C | 0.03 |
| Cr | 19 |
| Mn | 0.9 |
| Mo | 2.6 |
| Ni | 11.5 |
| Si | 0.8 |
Mechanical properties
| Tensile strength (Rm) | 540–670 MPa |
|---|---|
| Yield strength (Rp0.2) | 355 MPa |
| Elongation (A5) | 30 % |
| Impact energy (KV) | 47 J (20 °C) |
Process
| Polarity | DC+/AC |
|---|---|
| Positions | PAflatPBhorizontal-verticalPChorizontalPDhorizontal-overheadPEoverheadPFvertical-up |
| Re-drying | 120–200 °C / ≥2 h |
Sizes and part numbers
| Ø | Length | Current | Request |
|---|---|---|---|
| 2.5 mm | 250 mm | 50–90 A | |
| 3.2 mm | 350 mm | 80–120 A | |
| 4 mm | 350 mm | 110–160 A |
Cross-reference
| Replaces FOX EAS 4 M (Böhler) | Direct replacement |
| Replaces FOX EAS 4 M-A (Böhler) | Direct replacement |
| Replaces EutecTrode 316L-17 (Castolin) | Direct replacement |
| Replaces EutecTrode 316L-16 (Castolin) | Direct replacement |
| Replaces EutecTrode 316LVD-17 (Castolin) | Direct replacement |
| Replaces OK 63.30 (ESAB) | Direct replacement |
| Replaces OK 63.20 (ESAB) | Direct replacement |
| Replaces OK 63.35 (ESAB) | Direct replacement |
| Replaces S-316L.16N (Hyundai) | Direct replacement |
| Replaces NC-36L (Kobelco) | Direct replacement |
| Replaces Arosta 316L (Lincoln) | Direct replacement |
| Replaces Limarosta 316L (Lincoln) | Direct replacement |
| Replaces Excalibur 316/316L-16 (Lincoln) | Direct replacement |
| Replaces EI 316L (Magmaweld) | Direct replacement |
| Replaces AS P-316L (Askaynak) | Direct replacement |
| Replaces NIC 316 L (Nicrotec) | Direct replacement |
| Replaces NIC 506 (Nicrotec) | Direct replacement |
| Replaces CLEARINOX E 316L (Oerlikon) | Direct replacement |
| Replaces SUPRANOX 316L (Oerlikon) | Direct replacement |
| Replaces SUPRANOX RS 316L (Oerlikon) | Direct replacement |
| Replaces 20/10MBC (Selectarc) | Direct replacement |
| Replaces INOX 316L (Selectarc) | Direct replacement |
| Replaces 316VD (Selectarc) | Direct replacement |
| Replaces INOX 316NG (Selectarc) | Direct replacement |
| Replaces 316HR (Selectarc) | Direct replacement |
| Replaces UTP 68 MoLC (UTP) | Direct replacement |
| Replaces WA TETRA V 316L-E (Welding Alloys) | Direct replacement |
Equivalence refers to the classification (AWS / EN ISO), not to product identity. In applications with a qualified procedure (WPS), validate the substitution before use.
Advantages
- Acid and corrosion resistant.
- Service to 400°C.
- All positions except vertical-down.