High-strength steels
FERVEO HTS 620 TIG
TIG rodCatalogue only
also as: solid wireflux-cored wire (FCW)
AWS class
EN ISO 16834-A Mn3Ni1Mo
EN ISO class
G 62 6 M/C Mn3Ni1Mo
Tensile strength (Rm)
700–890 MPa
Classification
| AWS class | EN ISO 16834-A Mn3Ni1Mo |
|---|---|
| EN ISO class | G 62 6 M/C Mn3Ni1Mo |
Purpose
- Low-alloy Mn-Ni-Mo TIG rod for high-elastic-limit steel (EN ISO 16834-A Mn3Ni1Mo, EN ISO G 62 6 M/C Mn3Ni1Mo) — the entry point of the Dratec solid-rod range in the FERVEO HTS ladder.
Why it works
The Mn-Ni-Mo alloy in solid-rod form gives the same kind of elevated mechanical strength as the FERVEO HTS electrode range, here for the manual TIG process — it needs moderate preheat before welding.
Fields of application
- High-elastic-limit and low-alloy Cr-Ni-Mo steel (N-A-XTRA 55-60-65-70 and equivalents), with preheat between 100°C and 200°C.
Chemical composition
| Element | Typical, % |
|---|---|
| C | 0.08 |
| Mn | 1.8 |
| Mo | 0.4 |
| Ni | 1 |
| Si | 0.6 |
Mechanical properties
| Tensile strength (Rm) | 700–890 MPa |
|---|---|
| Yield strength (Rp0.2) | 620 MPa |
| Elongation (A5) | 20 % |
Process
Sizes and part numbers
| Ø | Request |
|---|---|
| 1 mm | |
| 1.6 mm | |
| 2.4 mm | |
| 3.2 mm |
Base metals
St 52St 50St 60St 70StE420-StE 690N-A-XTRA 56-63-70S550QL-S620QLP550M15NiCuMoNb520MnMoNi55
Advantages
- TIG process — higher productivity than a covered electrode in semi-automatic shop welding.
Limitations
- Requires preheat between 100°C and 200°C before welding — unlike some FERVEO HTS ladder electrodes that don't call for it explicitly.
- For higher mechanical strength in solid-rod form, see FERVEO HTS 690 MIG and above.