Tool steels
FERVEO TLS 2343 MIG
solid wireCatalogue only
also as: TIG rod
AWS class
EN 14700 S Fe 3
EN ISO class
S Fe 3
Hardness
570 HB · 52–57 HRC
Classification
| AWS class | EN 14700 S Fe 3 |
|---|---|
| EN ISO class | S Fe 3 |
Purpose
- Cr-Mo solid wire (S Fe 3) for surfacing hot-work tool steel, 52-57 HRC hardness.
- Repair and new manufacture of tooling for service up to 500°C: continuous-casting rolls, hot-shear blades, die-casting molds, dies.
Why it works
Chromium (5%) and molybdenum (1.1%) on a medium-high carbon base (0.38%) produce a martensitic deposit with stable secondary hardness at elevated service temperature — this tempering resistance is what lets the die hold its hardness through repeated heating cycles in service, instead of softening after the first few hours of use.
Fields of application
- Continuous-casting rolls, hot-shear blades, die-casting molds, dies.
- Repair and new manufacture of hot-work tooling for service up to 500°C.
Chemical composition
| Element | Typical, % |
|---|---|
| C | 0.38 |
| Cr | 5 |
| Mn | 0.4 |
| Mo | 1.1 |
| Si | 1 |
Mechanical properties
| Hardness | 570 HB · 52–57 HRC |
|---|
Process
| Polarity | DC+ |
|---|---|
| Shielding gas | M1,M2,M3 |
Sizes and part numbers
| Ø | Request |
|---|---|
| 0.8 mm | |
| 1 mm | |
| 1.2 mm | |
| 1.6 mm |
Supply programme
spools D100 / D200 / K200 / K300
Advantages
- Stable secondary hardness — resists tempering through repeated in-service heating cycles.
- Continuous service up to 500°C.
Limitations
- Hardness (52-57 HRC) lower than TLS 2606 or TLS 3348 — not this datasheet's highest-wear-resistance option.