Aluminium
FERVEO ALU 5754 MIG
solid wireCatalogue only
also as: TIG rod
AWS class
ER 5754
EN ISO class
EN ISO 18273 (2016) : Al 5754 - AlMg3
Tensile strength (Rm)
200 MPa
Classification
| AWS class | ER 5754 |
|---|---|
| EN ISO class | EN ISO 18273 (2016) : Al 5754 - AlMg3 |
Purpose
- Al-Mg (3% Mg) solid wire for joining aluminum-magnesium alloys, especially parts intended for anodizing.
- Moderate Mg content — good finish after anodizing, unlike this datasheet's Al-Si wires.
Why it works
Magnesium (3%) instead of silicon gives a deposit that anodizes to a uniform tone close to the base metal — the reason it's chosen specifically for parts where the anodized finish matters, something the Al-Si wires (ALU 4043/4047) can't offer.
Fields of application
- Joining aluminum-magnesium alloys (DIN 3.3206, 3.3315, 3.3525 and equivalents).
- Parts intended for anodizing where a uniform finish tone matters.
Chemical composition
| Element | Typical, % |
|---|---|
| Al | balance |
| Mg | 3 |
| Mn | 0.3 |
| Ti | 0.13 |
Mechanical properties
| Tensile strength (Rm) | 200 MPa |
|---|---|
| Yield strength (Rp0.2) | 80 MPa |
| Elongation (A5) | 20 % |
Process
| Polarity | DC+ |
|---|---|
| Shielding gas | I1 |
Sizes and part numbers
| Ø | Request |
|---|---|
| 0.8 mm | |
| 1 mm | |
| 1.2 mm | |
| 1.6 mm |
Supply programme
spools D100 / D200 / K200 / K300
Cross-reference
| Replaces ALUFIL AlMg3 (Oerlikon) | Direct replacement |
Equivalence refers to the classification (AWS / EN ISO), not to product identity. In applications with a qualified procedure (WPS), validate the substitution before use.
Base metals
3.32063.33153.35253.35353.35373.3541
Advantages
- Anodizes to a uniform tone, unlike this datasheet's Al-Si wires.
- Higher ductility (A5 20%) than ALU 4043/4047.
Limitations
- Lower mechanical strength (Rm 200 MPa) than ALU 5356 or ALU 5183 — not this datasheet's highest-strength structural option.
- Moderate Mg (3%) — doesn't provide the highest strength in this datasheet's Al-Mg family, see ALU 5356/5183/5087 for that.