Mild & carbon steels
FERVEO STL ZR TIG
TIG rodCatalogue only
also as: solid wire
AWS class
EN ISO 14341 G2Ti
EN ISO class
-G2Ti
Tensile strength (Rm)
560 MPa
Classification
| AWS class | EN ISO 14341 G2Ti |
|---|---|
| EN ISO class | -G2Ti |
Purpose
- Solid MIG rod with triple Al-Ti-Zr deoxidation, especially suited to galvanized steel (EN ISO 14341 G2Ti).
Why it works
The combination of aluminum, titanium and zirconium as deoxidizers controls slag formation and gives a flat bead even on galvanized steel — welding before galvanizing is recommended whenever possible, for the best result.
Fields of application
- Metal carpentry and boilermaking in Fe42-Fe52 type steel, with very good results on galvanized steel.
Chemical composition
| Element | Typical, % |
|---|---|
| C | 0.06 |
| Al | 0.1 |
| Mn | 1.1 |
| Si | 0.5 |
| Ti | 0.1 |
| Zr | 0.1 |
Mechanical properties
| Tensile strength (Rm) | 560 MPa |
|---|---|
| Yield strength (Rp0.2) | 480 MPa |
| Elongation (A5) | 27 % |
| Impact energy (KV) | 100 J |
Process
Sizes and part numbers
| Ø | Request |
|---|---|
| 1 mm | |
| 1.6 mm | |
| 2.4 mm | |
| 3.2 mm |
Supply programme
rods 0.8–1.2 mm
Base metals
St 33-St 52.3StE255-StE 500HI-HIIC10-C35St2St3St4
Advantages
- Very good behavior on galvanized steel — contained slag formation and a flat bead.
- Compatible with the widest range of shielding gases in the FERVEO STL MIG family (M1, M2, M3, CO2).
Limitations
- Best result welding before galvanizing rather than on already-galvanized steel.