Copper & bronze
FERVEO CUP AL8NI6 MIG
solid wireCatalogue only
also as: TIG rod
AWS class
ERCuNiAl
EN ISO class
~ S Cu 6328 (CuAl9Ni5Fe3Mn2)
Hardness
180 HB
Classification
| AWS class | ERCuNiAl |
|---|---|
| EN ISO class | ~ S Cu 6328 (CuAl9Ni5Fe3Mn2) |
Purpose
- High-alloy aluminum-nickel bronze solid wire (CuAl9Ni5Fe3Mn2), excellent corrosion resistance — seawater-resistant surfacing.
Why it works
The higher nickel content (4.5%) versus CUP AL8NI2 MIG (2.2%) gives the best corrosion resistance in this datasheet's aluminum bronze family, along with the highest mechanical strength (Rm 650 MPa, hardness 180 HB) — the supplier explicitly highlights it for seawater-resistant surfacing.
Fields of application
- Joining copper-aluminum-nickel alloys.
- Seawater-resistant surfacing on unalloyed and low-alloy steels, and cast steel parts.
Chemical composition
| Element | Typical, % |
|---|---|
| Al | 8.5 |
| Cu | balance |
| Fe | 3.5 |
| Mn | 0.8 |
| Ni | 4.5 |
Mechanical properties
| Tensile strength (Rm) | 650 MPa |
|---|---|
| Yield strength (Rp0.2) | 380 MPa |
| Elongation (A5) | 10 % |
| Hardness | 180 HB |
Process
| Polarity | DC+ |
|---|---|
| Shielding gas | I1 |
Sizes and part numbers
| Ø | Request |
|---|---|
| 0.8 mm | |
| 1 mm | |
| 1.2 mm | |
| 1.6 mm |
Supply programme
spools D100 / D200 / K200 / K300 · Ø 0.8 / 1 / 1.2 / 1.6 mm
Base metals
2.09622.09662.09702.09712.09752.09782.0980
Advantages
- Excellent corrosion resistance — the highest nickel content in the CUP AL family.
- The highest mechanical strength in the family (Rm 650 MPa, 180 HB).
- Explicitly recommended for seawater service.
Limitations
- Not suitable for oxy-fuel gas welding.
- Reduced ductility (A5 10%) due to the high strength.